PC Kingfa JH830 Kingfa
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Kingfa/Kingfa JH830 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 600 J/m |
| Suspended wall beam without notch impact strength | 23°C,3.20mm | ASTM D256 | 无断裂 |
| hardness | Test Condition | Test Method | Kingfa/Kingfa JH830 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 120 |
| Electrical performance | Test Condition | Test Method | Kingfa/Kingfa JH830 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| Surface Resistivity | ASTM D257 | 1E+15 ohms | |
| dielectric strength | 1.60mm | ASTM D149 | 28 kV/mm |
| Mechanical properties | Test Condition | Test Method | Kingfa/Kingfa JH830 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 60 % |
| tensile strength | ASTM D638 | 60.0 MPa | |
| Flexural modulus | ASTM D790 | 2380 MPa | |
| bending strength | ASTM D790 | 85.0 MPa |
| flammability | Test Condition | Test Method | Kingfa/Kingfa JH830 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| Hot filament ignition temperature | 1.6mm | IEC 60695-2-13 | 950 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Kingfa/Kingfa JH830 |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ASTM D955 | 0.50to0.70 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.15 % |
| density | ASTM D792 | 1.21 g/cm³ |
| Thermal performance | Test Condition | Test Method | Kingfa/Kingfa JH830 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 125 °C |
| 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 136 °C |