PC EXL9414-BK1A068 SABIC INNOVATIVE NANSHA
LEXAN™
Plastic bag,Quick charging phone case
High mobility,High ductility at low tem
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL9414-BK1A068 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 75 kJ/m² |
-30°C | ISO 179/1eA | 29 kJ/m² | |
Dart impact | 23°C, Total Energy | ASTM D3763 | 67.0 J |
hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL9414-BK1A068 |
---|---|---|---|
Rockwell hardness | L 计秤 | ASTM D785 | 83 |
R 级 | ASTM D785 | 117 |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL9414-BK1A068 |
---|---|---|---|
Tensile modulus | --2 | ASTM D638 | 2110 Mpa |
tensile strength | 屈服3 | ASTM D638 | 56.0 Mpa |
elongation | 断裂3 | ASTM D638 | 110 % |
断裂 | ISO 527-2/50 | 110 % | |
Flexural modulus | --5 | ISO 178 | 2180 Mpa |
bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 88.0 Mpa |
--5,6 | ISO 178 | 86.0 Mpa | |
Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2190 Mpa |
tensile strength | 断裂 | ISO 527-2/50 | 60.0 Mpa |
屈服 | ISO 527-2/50 | 57.0 Mpa | |
elongation | 屈服 | ISO 527-2/50 | 5.6 % |
屈服3 | ASTM D638 | 5.8 % | |
tensile strength | 断裂3 | ASTM D638 | 62.0 Mpa |
Tensile modulus | -- | ISO 527-2/1 | 2140 Mpa |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL9414-BK1A068 |
---|---|---|---|
Dissipation Factor | 1.10 GHz | ASTM ES7-83 | 6.0E-3 |
dielectric strength | 3.20 mm, in Oil | ASTM D149 | 13 KV/mm |
Volume resistivity | ASTM D257 | > 1.0E+16 ohms·cm | |
Surface Resistivity | ASTM D257 | > 1.0E+16 ohms | |
dielectric constant | 1.10 GHz | ASTM ES7-83 | 2.78 |
flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL9414-BK1A068 |
---|---|---|---|
UL flame retardant rating | 3.1 mm | UL 94 | 5VA |
1.0 mm | UL 94 | V-0 | |
0.8 mm | UL 94 | V-1 | |
Hot filament ignition temperature | 1.0 mm | IEC 60695-2-13 | 850 °C |
UL flame retardant rating | 1.5 mm | UL 94 | 5VB |
0.50 mm | UL 94 | V-2 | |
Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 960 °C |
Limiting Oxygen Index | ISO 4589-2 | 39 % |
physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL9414-BK1A068 |
---|---|---|---|
Shrinkage rate | 横向流动 : 3.20 mm | 内部方法 | 0.40 - 0.80 % |
Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 10.0 cm3/10min |
melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 12 g/10 min |
Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.40 - 0.80 % |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL9414-BK1A068 |
---|---|---|---|
Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 6.9E-5 cm/cm/°C |
vicat | -- | ISO 306/B120 | 138 °C |
Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距9,HDT | ISO 75-2/Ae | 117 °C |
Linear coefficient of thermal expansion | 横向 : 23 到 80°C | ISO 11359-2 | 7.6E-5 cm/cm/°C |
流动 : 23 到 80°C | ISO 11359-2 | 7.4E-5 cm/cm/°C | |
vicat | -- | ISO 306/B50 | 136 °C |
Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距9,HDT | ISO 75-2/Be | 131 °C |
0.45 MPa, 未退火, 3.20 mm,HDT | ASTM D648 | 134 °C | |
Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 7.3E-5 cm/cm/°C |
Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm,HDT | ASTM D648 | 118 °C |
injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL9414-BK1A068 |
---|---|---|---|
screw speed | 40 to 70 rpm | ||
Suggested maximum moisture content | 0.020 % | ||
Processing (melt) temperature | 295 to 315 °C | ||
drying temperature | 120 °C | ||
Suggested injection volume | 40 to 60 % | ||
drying time | 3.0 to 4.0 hr | ||
Temperature in the middle of the barrel | 280 to 305 °C | ||
Temperature at the rear of the barrel | 270 to 295 °C | ||
Exhaust hole depth | 0.025 to 0.076 mm | ||
Temperature at the front of the material cylinder | 295 to 315 °C | ||
Back pressure | 0.300 to 0.700 Mpa | ||
Temperature | 70 to 95 °C | ||
Spray nozzle temperature | 290 to 310 °C |