Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 1202 ASAHI JAPAN
Leona™
Electrical applications
Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | ASAHI JAPAN/1202 |
|---|---|---|---|
| Limiting Oxygen Index | 干 | ASTM D2863 | 26 % |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/1202 |
|---|---|---|---|
| Water absorption rate | 湿 | 2.5 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/1202 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干/湿 | ASTM D256 | 39/147 J/m |
| Rockwell hardness | 干/湿 | ASTM D785 | 120/108 R scale |
| elongation at break | 干/湿 | ASTM D638 | 50/250 % |
| tensile strength | 干/湿 | ASTM D638 | 79/57 Mpa |
| bending strength | 干/湿 | ASTM D790 | 118/54 Mpa |
| flexural coefficient | 干/湿 | ASTM D790 | 2.8/1.2 GPa |
| Rockwell hardness | 干/湿 | ASTM D785 | 80/55 M-scale |
| Wear factor | 湿 | ASTM D1044 | 7 |
| physical property | Test Condition | Test Method | ASAHI JAPAN/1202 |
|---|---|---|---|
| Shrinkage rate | 干 | 旭化成方法 | 1.3-2.0 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/1202 |
|---|---|---|---|
| specific heat | 干 | 1670 J/(kg.k) | |
| Linear coefficient of thermal expansion | 干 | ASTM D696 | 8 |
| Heat distortion temperature | 0.46MPa,干，HDT | ASTM D648 | 230 °C |
| thermal conductivity | 0.2 W/(m.K) | ||
| Heat distortion temperature | 1.82MPa,干，HDT | ASTM D648 | 70 °C |
| UL flame retardant rating | UL 94 | V-2 |