PC CFR9111-NA8G001T SABIC INNOVATIVE NANSHA
LEXAN™ 
Electronic and Electrical Applications,Plastic bag,Lighting applications,Electrical appliances
Non chloro non bromine fl
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR9111-NA8G001T
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648130 °C
1.8 MPa, Unannealed, 3.20 mmASTM D648120 °C
0.45 MPa, Unannealed, 4.00 mm, 100 mm Span9ISO 75-2/Be131 °C
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9ISO 75-2/Ae121 °C
Linear coefficient of thermal expansionAcross Flow : 23 to 80°CISO 11359-28.0E-5 cm/cm/°C
Flow : -40 to 40°CASTM E8316.8E-5 cm/cm/°C
Across Flow : -40 to 40°CASTM E8317.0E-5 cm/cm/°C
Flow : 23 to 80°CISO 11359-27.7E-5 cm/cm/°C
RTIUL 746130 °C
RTI ElecUL 746130 °C
RTI ImpUL 746120 °C
Vicat softening temperature--ISO 306/B120140 °C
--ISO 306/B50139 °C
--ASTM D152510136 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR9111-NA8G001T
Bending modulus--5ISO 1782400 Mpa
50.0 mm Span4ASTM D7902400 Mpa
bending strengthYield, 50.0 mm Span4ASTM D790103 Mpa
--5,6ISO 17896.0 Mpa
elongationYieldISO 527-2/506.0 %
Yield3ASTM D6386.0 %
Break3ASTM D63880 %
BreakISO 527-2/5073 %
Tensile modulus--2ASTM D6382400 Mpa
--ISO 527-2/12300 Mpa
tensile strengthYieldISO 527-2/5063.0 Mpa
BreakISO 527-2/5057.0 Mpa
Break3ASTM D63854.0 Mpa
Yield3ASTM D63867.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR9111-NA8G001T
Dielectric constant1.10 GHzASTM ES7-832.79
Dissipation factor1.10 GHzASTM ES7-835.6E-3
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR9111-NA8G001T
melt mass-flow rate300°C/1.2 kgASTM D123818 g/10 min
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113317.0 cm3/10min
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.60 - 0.80 %
Flow : 3.20 mmInternal Method0.55 - 0.75 %
Water absorption rateSaturation, 23°CISO 620.13 %
Equilibrium, 23°C, 50% RHISO 620.11 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR9111-NA8G001T
Charpy Notched Impact Strength23°CISO 179/1eA59 kJ/m²
-30°CISO 179/1eA10 kJ/m²
Dart impact23°C, Total EnergyASTM D376380.0 J
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CASTM D4812无断裂
-30°CASTM D4812无断裂
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR9111-NA8G001T
Burning wire flammability index1.5 mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.5 mmIEC 60695-2-13850 °C
UL flame retardant rating0.40 mmUL 94V-2
1.2 mmUL 94V-1
1.5 mmUL 94V-0
optical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR9111-NA8G001T
transmissivity3000 μmInternal Method> 88.0 %
2000 μmInternal Method> 89.0 %
1000 μmInternal Method> 90.0 %
injectionTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR9111-NA8G001T
Back pressure0.300 to 0.700 Mpa
drying temperature120 °C
drying time3.0 to 4.0 hr
Exhaust hole depth0.025 to 0.076 mm
Mold temperature70 to 95 °C
Processing (melt) temperature280 to 305 °C
Screw speed40 to 70 rpm
Spray nozzle temperature275 to 300 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
Temperature at the front of the material cylinder280 to 305 °C
Temperature at the rear of the barrel260 to 280 °C
Temperature in the middle of the barrel270 to 295 °C