PC HFD1810 NA9E108T SABIC INNOVATIVE NANSHA
LEXAN™ 
Automotive sector、Electronic field、Electrical field
High mobility、copolymer
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
Charpy Notched Impact Strength23°CISO 179/1eA64 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA13 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376356.0 J
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Dart impact--ISO 6603-295.0 J
hardnessTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
Rockwell hardnessR 级ASTM D785120
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
Tensile modulus--2ASTM D6382270 Mpa
tensile strength 屈服3ASTM D63860.0 Mpa
elongation断裂3ASTM D638130 %
断裂ISO 527-2/5097 %
Flexural modulus--5ISO 1782180 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D790100 Mpa
--5,6ISO 17891.0 Mpa
Flexural modulus50.0 mm 跨距4ASTM D7902240 Mpa
tensile strength 断裂ISO 527-2/5056.0 Mpa
屈服ISO 527-2/5063.0 Mpa
elongation屈服ISO 527-2/506.0 %
屈服3ASTM D6385.5 %
tensile strength 断裂3ASTM D63856.0 Mpa
Tensile modulus--ISO 527-2/12180 Mpa
optical performance Test ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
refractive indexASTM D5421.582
transmissivity2540 µmASTM D100388.0 %
Haze ratio2540 µmASTM D1003< 1.0 %
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
UL flame retardant rating1.0 mmUL 94V-2
0.30 mmUL 94HB
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
Water absorption rate平衡, 23°C, 50% RHISO 620.15 %
Melt volume flow rate300°C/1.2 kgISO 113338.0 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D123840 g/10 min
Water absorption rate饱和, 23°CISO 620.30 %
Shrinkage rate3.20 mm，Flow内部方法0.50 - 0.70 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8318.0E-5 cm/cm/°C
横向 : -40°CISO 11359-28.0E-5 cm/cm/°C
Heat distortion temperature0.45 MPa, 未退火, 3.20 mm，HDTASTM D648121 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
RTIUL 746105 °C
vicat--ISO 306/B120130 °C
--ASTM D152510135 °C
--ISO 306/B50129 °C
Heat distortion temperature1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDTISO 75-2/Af115 °C
RTI ImpUL 746105 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8318.0E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D648110 °C
RTI ElecUL 746105 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
drying time3.0 to 4.0 hr
screw speed35 to 75 rpm
Temperature in the middle of the barrel250 to 295 °C
Temperature at the rear of the barrel240 to 280 °C
Processing (melt) temperature260 to 305 °C
Exhaust hole depth0.038 to 0.076 mm
drying temperature105 to 110 °C
Suggested injection volume40 to 60 %
Temperature at the front of the material cylinder260 to 305 °C
Back pressure0.300 to 0.700 Mpa
Temperature50 to 80 °C
Spray nozzle temperature255 to 300 °C