PC LS-2250 TEIJIN JAPAN
PANLITE®
Engineering accessories
wear resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN JAPAN/LS-2250 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | NoBreak |
| thermal performance | Test Condition | Test Method | TEIJIN JAPAN/LS-2250 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 130 °C |
| RTI Imp | 1.5mm | UL 746 | 105 °C |
| Heat Deflection Temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 139 °C |
| RTI Elec | 1.5mm | UL 746 | 115 °C |
| vicat | ISO 306/B50 | 141 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| MD | ISO 11359-2 | 7E-05 cm/cm/°C | |
| RTI Str | 1.5mm | UL 746 | 105 °C |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/LS-2250 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2400 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 50.0 Mpa |
| Elongation at break | ASTM D638/ISO 527 | 51 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 50.0 Mpa |
| bending strength | ISO 178 | 80.0 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 55(560) kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 78(800) % | |
| flexural modulus | ISO 178 | 2200 Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 2300(23500) kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 290(30) kg·cm/cm(J/M)ft·lb/in | |
| Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
| 屈服 | ISO 527-2/50 | 6.0 % |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/LS-2250 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 3.00 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
| other | Test Condition | Test Method | TEIJIN JAPAN/LS-2250 |
|---|---|---|---|
| characteristic | 耐磨擦磨损型 |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/LS-2250 |
|---|---|---|---|
| shrinkage rate | MD:4.00mm | 内部方法 | 0.50-0.70 % |
| density | ASTM D792/ISO 1183 | 1.26 | |
| shrinkage rate | TD:4.00mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.17 % |
| ASTM D570/ISO 62 | 0.17 % |
| flammability | Test Condition | Test Method | TEIJIN JAPAN/LS-2250 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |