Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC AC9140-A7 FCFC TAIWAN
TAIRILITE®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | FCFC TAIWAN/AC9140-A7 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eA | 48 kJ/m² |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 9 kJ/m² |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC9140-A7 |
|---|---|---|---|
| Flexural modulus | 23℃ | ISO 178 | 1400 Mpa |
| Rockwell hardness | M计称 | ISO 2039-2 | 100 |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 190 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.8 % |
| bending strength | 23℃ | ISO 178 | 280 Mpa |
| Flame retardant performance | Test Condition | Test Method | FCFC TAIWAN/AC9140-A7 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0.5VA |
| 1.5mm | UL 94 | V-0 | |
| 0.75mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AC9140-A7 |
|---|---|---|---|
| Shrinkage rate | 普通 | ISO 294-4 | 0.2-0.6 % |
| 横向 | ISO 294-4 | 0.4-0.6 % | |
| density | ASTM D1183 | 1.65 | |
| Water absorption rate | 饱和，23℃ | ISO 62 | 0.02 % |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC9140-A7 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 280 °C | |
| Heat distortion temperature | 1.8 MPa，未退火，HDT | ISO 75-2/A | 270 °C |
| 8 MPa，未退火，HDT | ISO 75-2/A | 200 °C | |
| Glass Transition Temperature | ISO 11357-2 | 90 °C |