LCP S475 BK210P TAIWAN POLYPLASTICS
LAPEROS®
Electrical applications、Home appliance components
Low warpage、High mobility、heat-resisting、Flame retardant、enhance、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIWAN POLYPLASTICS/S475 BK210P |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | TAIWAN POLYPLASTICS/S475 BK210P |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 180 Mpa |
| Flexural modulus | 23°C | ISO 178 | 12000 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 135 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.8 % |
| Fracture bending strain | ISO 178 | 2.4 % | |
| Tensile modulus | ISO 527-2/1A | 12300 Mpa |
| Electrical performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/S475 BK210P |
|---|---|---|---|
| Dissipation Factor | 1 MHz | IEC 60250 | 8.0E-3 |
| relative permittivity | 1 MHz | IEC 60250 | 3.70 |
| flammability | Test Condition | Test Method | TAIWAN POLYPLASTICS/S475 BK210P |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TAIWAN POLYPLASTICS/S475 BK210P |
|---|---|---|---|
| Shrinkage rate | 流量 | ISO 294-4 | 0.0 % |
| 横向流量 | ISO 294-4 | 0.40 % |
| Thermal performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/S475 BK210P |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 350 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 305 °C |
| 8.0 MPa, 未退火，HDT | ISO 75-2/C | 213 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.0E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 2.5E-5 cm/cm/°C |
| injection | Test Condition | Test Method | TAIWAN POLYPLASTICS/S475 BK210P |
|---|---|---|---|
| drying time | 6.0 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Temperature in the middle of the barrel | 340 to 360 °C | ||
| Temperature at the rear of the barrel | 330 to 350 °C | ||
| Processing (melt) temperature | 360 to 375 °C | ||
| Hopper temperature | 20 to 40 °C | ||
| drying temperature | 150 °C | ||
| Temperature at the front of the material cylinder | 345 to 365 °C | ||
| Back pressure | < 3.00 Mpa | ||
| Temperature | 80 to 120 °C | ||
| injection speed | 中等 | ||
| Spray nozzle temperature | 355 to 370 °C |