PBT HR5330HF BK503 DUPONT USA
Cristin® 
Electronic and electrical components
Hydrolysis resistance,Filler: Glass fiber reinf,30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDUPONT USA/HR5330HF BK503
Charpy Notched Impact Strength23°CISO 179/1eA13 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U65 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA12 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU70 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A14 kJ/m²
-40°CISO 180/1A11 kJ/m²
thermal performanceTest ConditionTest MethodDUPONT USA/HR5330HF BK503
Heat Deflection Temperature0.45MPa,未退火，HDTISO 75-2/B221 °C
Linear coefficient of thermal expansionMD：--ISO 11359-22E-05 cm/cm/°C
MD：55to160°CISO 11359-21.5E-05 cm/cm/°C
melting temperatureISO 11357-3225 °C
Heat Deflection Temperature1.8MPa,未退火，HDTISO 75-2/A207 °C
1.80 Mpa，未退火，HDTISO 75B-1207 ℃
melting temperatureISO 3146225 ℃
Linear coefficient of thermal expansionTD：-40to23°CISO 11359-29E-05 cm/cm/°C
Heat Deflection Temperature0.45 Mpa，未退火，HDTISO 75B-1221 ℃
vicatISO 306/B50215 °C
Linear coefficient of thermal expansionMD：-40to23°CISO 11359-22.5E-05 cm/cm/°C
TD：55to160°CISO 11359-21.5E-04 cm/cm/°C
TD：--ISO 11359-21.5E-04 cm/cm/°C
Mechanical propertiesTest ConditionTest MethodDUPONT USA/HR5330HF BK503
Tensile modulusISO 527-28500 Mpa
bending strength23℃ISO 178203 MPa
Impact strength of cantilever beam gap23 ℃, Type 1, Notch AISO 18016.3 KJ/m
Tensile stress23℃，屈服ISO 527-1134 MPa
Impact strength of simply supported beam without notch23 ℃, Type 1, EdgewiseISO 17975.1 KJ/m
tensile strength断裂ISO 527-2132 Mpa
Charpy Notched Impact Strength-30 ℃, Type 1, Edgewise, Notch AISO 17911.5 KJ/m
flexural modulus23℃ISO 1787800 MPa
Poisson's ratioISO 5270.34
elongation23℃，屈服ISO 527-13.5 %
Tensile modulus23℃ISO 527-18500 MPa
bending strengthISO 178200 Mpa
Tensile strain断裂ISO 527-23.5 %
flexural modulusISO 1787700 Mpa
Charpy Notched Impact Strength23 ℃, Type 1, Edgewise, Notch AISO 17914.9 KJ/m
Impact strength of cantilever beam gap-40 ℃, Type 1, Notch AISO 18011.1 KJ/m
Electrical performanceTest ConditionTest MethodDUPONT USA/HR5330HF BK503
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 1
Dissipation Factor1kHzASTM D1507E-03
100HzASTM D1502.5E-03
1MHzASTM D1500.020
100HzIEC 602502.5E-03
relative permittivity100HzIEC 602504.40
dielectric strength1.00mm5IEC 60243-131 KV/mm
volume resistivityIEC 60093>1.0E+15 ohms·cm
dielectric strength--IEC 60243-144 KV/mm
relative permittivity1MHzIEC 602504.10
Surface ResistivityIEC 600931E+13 ohms
Dissipation Factor1MHzIEC 602500.020
Physical propertiesTest ConditionTest MethodDUPONT USA/HR5330HF BK503
Water absorption rate平衡,23°C,2.00mm,50%RHISO 620.15 %
viscosity numberISO 30795.0 cm³/g
ThermalConductivityofMelt0.28 W/m/K
FlowLength22.00mm，FlowLength350 mm
SpecificHeatCapacity of Melt1730 J/kg/°C
densityISO 11831.50 g/cm³
shrinkage rateTDISO 294-41.0 %
MediumDensity1.29 g/cm³
densityISO 11831.5 g/cm
Ejection Temperature170 °C
Water absorption rate饱和,23°C,2.00mmISO 620.35 %
shrinkage rateMDISO 294-40.30 %
flammabilityTest ConditionTest MethodDUPONT USA/HR5330HF BK503
UL flame retardant rating0.75mmUL 94HB
FMVSS flammabilityFMVSS302B
Flammability level0.75mmIEC 60695-11-10,-20HB
Limiting Oxygen IndexISO 4589-219 %
burning rate1.00mmISO 379530 mm/min