PA66 1433L TYNE USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TYNE USA/1433L |
|---|---|---|---|
| Impact strength of cantilever beam gap | 6.35mm | ASTM D256 | 80 J/m |
| hardness | Test Condition | Test Method | TYNE USA/1433L |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 101 |
| Mechanical properties | Test Condition | Test Method | TYNE USA/1433L |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 3.0 % |
| tensile strength | ASTM D638 | 165 MPa | |
| Flexural modulus | ASTM D790 | 9650 MPa | |
| Impact strength of cantilever beam gap | 6.35mm | ASTM D256 | 80 J/m |
| bending strength | ASTM D790 | 248 MPa |
| physical property | Test Condition | Test Method | TYNE USA/1433L |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 101 |
| Water absorption rate | 24hr | ASTM D570 | 0.70 % |
| density | ASTM D792 | 1.40 g/cm3 | |
| ASTM D792 | 1.40 g/cm³ | ||
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.20to0.40 % |
| 3.18mm | ASTM D955 | 0.20-0.40 % |
| Thermal performance | Test Condition | Test Method | TYNE USA/1433L |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 249 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 257 °C | |
| 1.8MPa,未退火，HDT | ASTM D648 | 249 ℃ | |
| 0.45MPa,未退火，HDT | ASTM D648 | 257 ℃ |