PC LN-1250G TEIJIN JAPAN
PANLITE®
Electrical field,Electronic field,Household appliances,Household appliances,Automotive External Parts
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | TEIJIN JAPAN/LN-1250G |
|---|---|---|---|
| Water absorption rate | 放置23°C水中24小时 | ISO 62 | 0.2 % |
| density | ISO 1183 | 1220 kg/m |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/LN-1250G |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 90 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2200 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 6 % | |
| Tensile modulus | 1mm/min | ISO 527-1 and ISO 527-2 | 2400 Mpa |
| compressive strength | ASTM D-695 | 78(800) MPa(Kgf/cm | |
| elongation at break | ASTM D638/ISO 527 | >50 % | |
| elongation at yield | 50mm/min | ISO 527-1 and ISO 527-2 | 6 % |
| tensile strength | ASTM D638/ISO 527 | 62 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 带缺口 | ISO 179 | 12 KJ/m |
| elongation at break | 50mm/min | ISO 527-1 and ISO 527-2 | >50 % |
| Tensile stress | 50mm/min | ISO 527-1 and ISO 527-2 | 62 Mpa |
| Impact strength of cantilever beam gap | 没缺口 | ISO 179 | NB KJ/m |
| Tensile modulus | ASTM D638/ISO 527 | 2400 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 12 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | 2mm/min | ISO 178 | 90 Mpa |
| Flexural modulus | 2mm/min | ISO 178 | 2200 Mpa |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/LN-1250G |
|---|---|---|---|
| Dielectric loss | 100Hz，正切 | IEC 60250 | 10 |
| 1MHz，正切 | IEC 60250 | 90 | |
| dielectric constant | 100Hz | IEC 60250 | 3.1 |
| Surface Resistivity | ASTM D257/IEC 60093 | ＞1x10^15 Ω | |
| arc resistance | IEC 60112 | 275 | |
| dielectric constant | ASTM D150/IEC 60250 | 3 | |
| Dielectric loss | ASTM D150/IEC 60250 | 90 | |
| dielectric strength | 短时间法 | IEC 60243-1 | 30 KV/m |
| dielectric constant | 1MHz | IEC 60250 | 3 |
| Volume resistivity | ASTM D257/IEC 60093 | ＞1x10^13 Ω.cm | |
| IEC 60093 | >1×10 Ω.cm | ||
| Surface Resistivity | IEC 60093 | >1×10 Ω |
| other | Test Condition | Test Method | TEIJIN JAPAN/LN-1250G |
|---|---|---|---|
| characteristic | 要求达-UL-940V-0级的电器电子元件 |
| optical performance | Test Condition | Test Method | TEIJIN JAPAN/LN-1250G |
|---|---|---|---|
| transmittance | ASTM D1003/ISO 13468 | 半透明 % |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/LN-1250G |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1220 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 11 300℃ 1.2KG g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| processability | Test Condition | Test Method | TEIJIN JAPAN/LN-1250G |
|---|---|---|---|
| Shrinkage rate | 垂直方向 | 本公司制订的测定法 | 0.5-0.7 % |
| 平行方向 | 本公司制订的测定法 | 0.5-0.7 % |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/LN-1250G |
|---|---|---|---|
| transmittance | 厚度3mm | ASTM D-1003 | 半透明 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/LN-1250G |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Linear coefficient of thermal expansion | 垂直方向 | ISO 11359-2 | 0.7 |
| vicat | 50℃/h 50N | ISO 308 | 148 °C |
| Heat distortion temperature | 1.80MPa，HDT | ISO 75-1 and ISO 75-2 | 129 °C |
| TEMPERATURE | 电学式，厚度1.47mm | UL 746B | 125 °C |
| Linear coefficient of thermal expansion | 平行方向 | ISO 11359-2 | 0.7 |
| TEMPERATURE | 非冲击式，厚度1.47mm | UL 746B | 125 °C |
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-1 and ISO 75-2 | 141 °C |
| TEMPERATURE | 冲击式，厚度1.47mm | UL 746B | 115 °C |