PC/ABS MB2213R MITSUBISHI ENGINEERING JAPAN
IUPILON™
Electronic and Electrical Applications
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2213R |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2213R |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 130 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 110 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2213R |
|---|---|---|---|
| bending strength | ISO 178 | 94.0 Mpa | |
| flexural modulus | ISO 178 | 2400 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 76 % | |
| Tensile modulus | ISO 527-2 | 2500 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.9 % |
| tensile strength | 屈服 | ISO 527-2 | 59.0 Mpa |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2213R |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 9.0 g/10min |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 9.00 cm3/10min |
| shrinkage rate | MD:3.20mm | 0.40-0.60 % | |
| TD:3.20mm | 0.40-0.60 % | ||
| 吸水率(饱和,23°C) | 0.12 % |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2213R |
|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL 94 | HB |