Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 RFL4536 SABIC INNOVATIVE NANSHA
LNP™ LUBRICOMP™
Automotive components、Electronic and electrical
Thermal stability、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/RFL4536 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 50 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 5.00 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.0 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 7.00 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/RFL4536 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 9800 Mpa | |
| ASTM D638 | 10500 Mpa | ||
| coefficient of friction | Static | ASTM D3702Modified | 0.48 |
| bending strength | ASTM D790 | 195 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 11.0 10^-10in^5-min/ft-lb-hr |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.56 |
| Flexural modulus | ASTM D790 | 7580 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/RFL4536 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/RFL4536 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.21 % |
| MD：24小时 | ASTM D955 | 0.20 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.78 % |
| 平衡,23°C,50%RH | ISO 62 | 1.2 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 1.0 % |
| TD:24小时 | ISO 294-4 | 0.97 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/RFL4536 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 236 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 233 °C |