Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT+PET 9K22117 4Plas
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 4Plas/ 9K22117 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 40 kJ/m² |
| 23°C | ISO 180/1U | 45 kJ/m² | |
| Impact strength of cantilever beam gap | -20°C | ISO 180/1A | 7.0 kJ/m² |
| -30°C | ISO 180/1A | 5.0 kJ/m² | |
| 23°C | ISO 180/1A | 7.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | 4Plas/ 9K22117 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.5 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 110 MPa |
| Tensile modulus | 23°C | ISO 527-2/5 | 6000 MPa |
| Electrical performance | Test Condition | Test Method | 4Plas/ 9K22117 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms |
| flammability | Test Condition | Test Method | 4Plas/ 9K22117 |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 750 °C |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | 4Plas/ 9K22117 |
|---|---|---|---|
| water content | ISO 960 | <1000 ppm | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| melt mass-flow rate | 270°C/2.16kg | ISO 1133 | 63 g/10min |
| density | ISO 1183 | 1.43 g/cm³ |
| Thermal performance | Test Condition | Test Method | 4Plas/ 9K22117 |
|---|---|---|---|
| vicat | ISO 306/B | 205 °C | |
| melting temperature | ISO 11357 | 220 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 210 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 190 °C |