Certificates
PP Homopolymer Fiberfil® J-60/30/F 美国舒尔曼
--
--
填料,玻璃纤维增强材料,30%,填料按重量,
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 美国舒尔曼/Fiberfil® J-60/30/F |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 80 J/m |
| hardness | Test Condition | Test Method | 美国舒尔曼/Fiberfil® J-60/30/F |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 105 |
| Mechanical properties | Test Condition | Test Method | 美国舒尔曼/Fiberfil® J-60/30/F |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 107 MPa |
| tensile strength | 23°C | ASTM D638 | 82.7 MPa |
| Tensile modulus | 23°C | ASTM D638 | 5860 MPa |
| Flexural modulus | 23°C | ASTM D790 | 4830 MPa |
| elongation | 屈服,23°C | ASTM D638 | 3.0 % |
| physical property | Test Condition | Test Method | 美国舒尔曼/Fiberfil® J-60/30/F |
|---|---|---|---|
| Shrinkage rate | MD：6.35mm | ASTM D955 | 0.40 % |
| Water absorption rate | 24hr | ASTM D570 | 0.030 % |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 6.0 g/10min |
| density | ASTM D792 | 1.12 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.30 % |
| Thermal performance | Test Condition | Test Method | 美国舒尔曼/Fiberfil® J-60/30/F |
|---|---|---|---|
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ASTM D648 | 152 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 157 °C |