Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MVLDPE SP1520 PRIME POLYMER JAPAN
EVOLUE™
Agricultural applications、chip、film、Agricultural applications、chip
High impact resistance、Low temperature thermal s
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | PRIME POLYMER JAPAN/SP1520 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 无断裂 |
| hardness | Test Condition | Test Method | PRIME POLYMER JAPAN/SP1520 |
|---|---|---|---|
| Shore hardness | 邵氏D,注塑 | ISO 868 | 54 |
| Basic performance | Test Condition | Test Method | PRIME POLYMER JAPAN/SP1520 |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 2 g/10min |
| Mechanical properties | Test Condition | Test Method | PRIME POLYMER JAPAN/SP1520 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | No Break | |
| tensile strength | 断裂,注塑 | ISO 527-2 | 16.0 Mpa |
| Tensile strain | 断裂,注塑 | ISO 527-2 | 350 % |
| Flexural modulus | 注塑 | ISO 178 | 160 Mpa |
| Tensile strain | Injection Molded，断裂 | ISO 527-2 | 350 % |
| Shore hardness | Shore D，Injection Molded | ISO 868 | 54 |
| physical property | Test Condition | Test Method | PRIME POLYMER JAPAN/SP1520 |
|---|---|---|---|
| Environmental stress cracking resistance | ASTM D1693 | >1000 hr | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.0 g/10min |
| Thermal performance | Test Condition | Test Method | PRIME POLYMER JAPAN/SP1520 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 116 ℃ | |
| ISO 11357-3 | 116 °C | ||
| vicat | ISO 306 | 96.0 °C | |
| ISO 306 | 96 ℃ |