Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA KIBILAC® PW-978B CHI MEI CORPORATION
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CHI MEI CORPORATION/KIBILAC® PW-978B |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 200 J/m |
| 23°C,6.40mm | ASTM D256 | 190 J/m | |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 6.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| 23°C | ISO 180/1A | 12 kJ/m² |
| hardness | Test Condition | Test Method | CHI MEI CORPORATION/KIBILAC® PW-978B |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 105 |
| Mechanical properties | Test Condition | Test Method | CHI MEI CORPORATION/KIBILAC® PW-978B |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 55 % |
| Flexural modulus | ASTM D790 | 2260 MPa | |
| tensile strength | 屈服 | ASTM D638 | 46.0 MPa |
| Flexural modulus | ISO 178 | 2100 MPa | |
| bending strength | ASTM D790 | 66.3 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 20 % |
| bending strength | ISO 178 | 67.0 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 47.0 MPa |
| 断裂 | ISO 527-2/50 | 34.0 MPa |
| flammability | Test Condition | Test Method | CHI MEI CORPORATION/KIBILAC® PW-978B |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | CHI MEI CORPORATION/KIBILAC® PW-978B |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 12.0 cm³/10min |
| density | 23°C | ISO 1183 | 1.07 g/cm³ |
| Shrinkage rate | ISO 294-4 | 0.40to0.70 % | |
| density | ASTM D792 | 1.07 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 13 g/10min |
| Thermal performance | Test Condition | Test Method | CHI MEI CORPORATION/KIBILAC® PW-978B |
|---|---|---|---|
| vicat | ASTM D15256 | 113 °C | |
| -- | ISO 306/A50 | 112 °C | |
| Heat distortion temperature | Unannealed，HDT | ASTM D648 | 93 °C |
| 1.8MPa,退火，HDT | ISO 75-2/A | 105 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 86.0 °C | |
| vicat | -- | ISO 306/B50 | 100 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9.1E-05 cm/cm/°C |
| Heat distortion temperature | Annealed，HDT | ASTM D648 | 103 °C |