Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI ATX200F-GY8119 SABIC INNOVATIVE US
ULTEM™
Bottle cap、Automotive Applications、Electrical applications
Hydrolysis resistance、High temperature resistan、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200F-GY8119 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 2100 J/m |
| Reverse notch impact | 3.20 mm | ASTM D256 | 2100 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200F-GY8119 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 70 % |
| bending strength | 屈服, 100 mm 跨距 | ASTM D790 | 144 Mpa |
| tensile strength | 屈服 | ASTM D638 | 96.0 Mpa |
| Flexural modulus | 100 mm 跨距 | ASTM D790 | 3170 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200F-GY8119 |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 0 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | |
| High arc combustion index (HAI) | UL 746 | PLC 4 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200F-GY8119 |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-2 |
| 1.5 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200F-GY8119 |
|---|---|---|---|
| melt mass-flow rate | 337°C/6.6 kg | ASTM D1238 | 24 g/10 min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200F-GY8119 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 190 °C |
| RTI Imp | UL 746 | 115 °C | |
| RTI | UL 746 | 115 °C | |
| RTI Elec | UL 746 | 115 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/ATX200F-GY8119 |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 350 to 370 °C | ||
| drying temperature | 135 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 4.0 to 6.0 hr | ||
| Temperature in the middle of the barrel | 345 to 365 °C | ||
| Temperature at the rear of the barrel | 340 to 360 °C | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 350 to 370 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 135 to 165 °C | ||
| Spray nozzle temperature | 350 to 370 °C |