PEEK Ketron® PEEK-HPV Mitsubishi Chemical Advanced Materials
--
Bearings, bushings
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Ketron® PEEK-HPV |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 25 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/1eA | 2.5 kJ/m² |
| hardness | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Ketron® PEEK-HPV |
|---|---|---|---|
| ball-indentation hardness | 10.0mm | ISO 2039-1 | 215 MPa |
| Rockwell hardness | M计秤,10.0mm | ISO 2039-2 | 85 |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Ketron® PEEK-HPV |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1B/1 | 5900 MPa | |
| Tensile strain | 断裂 | ISO 527-2/1B/5 | 5.0 % |
| tensile strength | 断裂 | ISO 527-2/1B/5 | 75.0 MPa |
| compression stress | 1%应变 | ISO 604/1 | 34.0 MPa |
| 2%应变 | ISO 604/1 | 67.0 MPa |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Ketron® PEEK-HPV |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 43 % |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Ketron® PEEK-HPV |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.14 % |
| 饱和,23°C | ISO 62 | 0.30 % | |
| 23°C,3.00mm4 | ISO 62 | 0.11 % | |
| density | ISO 1183 | 1.45 g/cm³ | |
| Water absorption rate | 23°C,24hr,3.00mm | ISO 62 | 0.050 % |
| 23°C,3.00mm2 | ISO 62 | 4.0 mg | |
| 23°C,3.00mm3 | ISO 62 | 9.0 mg |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Ketron® PEEK-HPV |
|---|---|---|---|
| Continuous use temperature | 溶融温度（DSC） | 340 °C | |
| Linear coefficient of thermal expansion | MD：23到150°C | 4E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 195 °C |
| Linear coefficient of thermal expansion | MD：23到100°C | 3.5E-05 cm/cm/°C | |
| Continuous use temperature | --5 | 250 °C | |
| --6 | 310 °C | ||
| Linear coefficient of thermal expansion | MD：导热系数(23°C) | 0.24 W/m/K | |
| MD：>150°C | 8.5E-05 cm/cm/°C |