PA6 DUPONT USA 73M40 NC010

Enhanced level

US$ 3,680 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	DUPONT USA/73M40 NC010
Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Tensile strain	Break	ISO 527-2	10 %
tensile strength	Break	ISO 527-2	87.0 Mpa
Tensile modulus		ISO 527-2	6000 Mpa
Tensile modulus			ASTM D638/ISO 527	6000 kg/cm²(MPa)[Lb/in²]
Bending modulus		ISO 178	5900 Mpa
Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
Bending modulus		ASTM D790/ISO 178	5900 kg/cm²(MPa)[Lb/in²]
flammability	Test Condition	Test Method	DUPONT USA/73M40 NC010
Flammability level	0.8mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	0.9mm	UL 94	HB
FMVSS flammability		FMVSS302	SE
other	Test Condition	Test Method	DUPONT USA/73M40 NC010
characteristic			低翘曲性热稳定性
Physical properties	Test Condition	Test Method	DUPONT USA/73M40 NC010
MediumDensity			1.28 g/cm³
Shrinkage rate	MD	ISO 294-4	0.80 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	5.4 %
Water absorption rate		Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.8 %
ThermalConductivityofMelt			0.27 W/m/K
Top out temperature			210 °C
SpecificHeatCapacity of Melt			1940 J/kg/°C
Shrinkage rate	TD	ISO 294-4	0.80 %
density		ASTM D792/ISO 1183	1.45
thermal performance	Test Condition	Test Method	DUPONT USA/73M40 NC010
Linear coefficient of thermal expansion	MD	ISO 11359-2	6.5E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	196 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	7.5E-05 cm/cm/°C
Combustibility (rate)		UL 94	HB
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	110 °C
Melting temperature		ISO 11357-3	221 °C
Vicat softening temperature		ISO 306/B50	210 °C
impact performance	Test Condition	Test Method	DUPONT USA/73M40 NC010
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	130 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	95 kJ/m²
Supplementary Information	Test Condition	Test Method	DUPONT USA/73M40 NC010
Odor		VDA270	3.50