Certificates
PA6 73M40 NC010 DUPONT USA
Zytel®
Automotive Applications、Electronic and electrical
Easy electroplating、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/73M40 NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 130 kJ/m² |
| -30°C | ISO 179/1eU | 95 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/73M40 NC010 |
|---|---|---|---|
| Odor | VDA270 | 3.50 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/73M40 NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 6000 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 5900 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 断裂 | ISO 527-2 | 10 % |
| Flexural modulus | ISO 178 | 5900 Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 6000 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 断裂 | ISO 527-2 | 87.0 Mpa |
| other | Test Condition | Test Method | DUPONT USA/73M40 NC010 |
|---|---|---|---|
| characteristic | 低翘曲性 热稳定性 |
| Physical properties | Test Condition | Test Method | DUPONT USA/73M40 NC010 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.45 |
| flammability | Test Condition | Test Method | DUPONT USA/73M40 NC010 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | SE | |
| Flammability level | 0.8mm | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | 0.9mm | UL 94 | HB |
| physical property | Test Condition | Test Method | DUPONT USA/73M40 NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.80 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 5.4 % |
| MediumDensity | 1.28 g/cm³ | ||
| Ejection Temperature | 210 °C | ||
| SpecificHeatCapacity of Melt | 1940 J/kg/°C | ||
| ThermalConductivityofMelt | 0.27 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.8 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/73M40 NC010 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| melting temperature | ISO 11357-3 | 221 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 196 °C |
| vicat | ISO 306/B50 | 210 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 110 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7.5E-05 cm/cm/°C |