Certificates
ABS/PA M/MK 20 A SCHULMAN USA
SCHULABLEND®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/M/MK 20 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 36 kJ/m² |
| hardness | Test Condition | Test Method | A SCHULMAN USA/M/MK 20 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 97.0 Mpa |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/M/MK 20 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 4900 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 77.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 4.5 % |
| flammability | Test Condition | Test Method | A SCHULMAN USA/M/MK 20 |
|---|---|---|---|
| burning rate | ISO 3795 | <100 mm/min | |
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | A SCHULMAN USA/M/MK 20 |
|---|---|---|---|
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 2.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/M/MK 20 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 101 °C |
| vicat | -- | ISO 306/A50 | 213 °C |
| -- | ISO 306/B50 | 128 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 179 °C |