PA6T C230N MITSUI CHEM JAPAN
ARLEN™
Electrical field、Electronic field
Glass fiber reinforced、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | MITSUI CHEM JAPAN/C230N |
|---|---|---|---|
| Glass Fiber Content | 30 % |
| Basic performance | Test Condition | Test Method | MITSUI CHEM JAPAN/C230N |
|---|---|---|---|
| Water absorption rate | 23℃,24小时在水里(2mmt,100℃) | ASTM D-570 | 0.3(3.0) % |
| Mechanical properties | Test Condition | Test Method | MITSUI CHEM JAPAN/C230N |
|---|---|---|---|
| elongation | dry(moist) | ASTM D-638 | 3(3) % |
| bending strength | ASTM D790/ISO 178 | 240(200) % | |
| Flexural modulus | dry(moist) | ASTM D-790 | 12000(8500) Mpa |
| ASTM D638/ISO 527 | 11000(8000) % | ||
| Rockwell hardness | ASTM D-785 | 110 M Scale | |
| tensile strength | dry(moist) | ASTM D-638 | 170(140) Mpa |
| elongation at break | ASTM D638/ISO 527 | 4(3) % | |
| Rockwell hardness | ASTM D785 | 95 | |
| tensile strength | ASTM D638/ISO 527 | 160(140) kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | dry(moist) | ASTM D-256 | 70(80) J/m |
| bending strength | dry(moist) | ASTM D-790 | 260(220) Mpa |
| Electrical performance | Test Condition | Test Method | MITSUI CHEM JAPAN/C230N |
|---|---|---|---|
| dielectric strength | dry | ASTM D-149 | 20 KV/mm |
| Dissipation Factor | 10 | ASTM D-150 | 0.012 |
| Volume resistivity | dry | ASTM D-257 | 10 Ω.cm |
| dielectric constant | 10 | ASTM D-150 | 3.9 |
| other | Test Condition | Test Method | MITSUI CHEM JAPAN/C230N |
|---|---|---|---|
| characteristic | 阻燃 |
| Physical properties | Test Condition | Test Method | MITSUI CHEM JAPAN/C230N |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.4(0.8) % | |
| density | ASTM D792/ISO 1183 | 1.63 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.3(3.0) % |
| physical property | Test Condition | Test Method | MITSUI CHEM JAPAN/C230N |
|---|---|---|---|
| Shrinkage rate | 2mmt | ASTM D-955 | 0.4(0.8) % |
| Thermal performance | Test Condition | Test Method | MITSUI CHEM JAPAN/C230N |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | HDT | ASTM D-648 | 295 °C |
| Linear coefficient of thermal expansion | ASTM D-696 | 2.4(5.0) | |
| melting temperature | 310 °C | ||
| 310 ℃（℉） | |||
| Glass transition temperature (Tg) | 85 °C | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 3.0(6.0) mm/mm.℃ | |
| UL flame retardant rating | UL 94 | V-0 |