PC 953A-116 SABIC INNOVATIVE NANSHA
LEXAN™
Casters、Household appliances
high viscosity、Flame retardant、UV resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/953A-116 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 70 - |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 65 cm-kgf/cm |
| Rockwell hardness | R级 | ASTM D785 | 118 - |
| tensile strength | TypeI,50mm/min | ASTM D638 | 560 Kgf/cm2 |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 326 cm-kgf/cm |
| Impact strength of cantilever beam gap | S型 | ASTM D1822 | 535 cm-kgf/cm² |
| bending strength | 1.3mm/min,50mm跨距 | ASTM D790 | 920 Kgf/cm2 |
| Flexural modulus | 1.3mm/min,50mm跨距 | ASTM D790 | 22800 Kgf/cm2 |
| Taber abraser | CS-17,1kg | ASTM D1044 | 10 mg/1000cy |
| Tensile strain | TypeI,50mm/min | ASTM D638 | 90 % |
| Dart impact (D3029), 23 ℃ | ASTM D3029 | 1728 cm-kgf |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/953A-116 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.E+17 ohm-cm | |
| HighAmpereArcIgn,surface{PLC} | UL 746A | PLC_2 | |
| Dissipation factor, 1MHz | ASTM D150 | 0.01 - | |
| Compared to the Leakage Traceability Index (CTI) | UL){PLC} | UL 746A | PLC_3 |
| Relative permittivity, 1MHz | ASTM D150 | 2.96 - | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR){PLC} | UL 746A | PLC 3 |
| Dielectric strength, in air, 3.2mm | ASTM D149 | 16.7 KV/mm | |
| Relative permittivity, 50/60Hz | ASTM D150 | 3.01 - | |
| Hot wire ignition (HWI) | HWI){PLC} | UL 746A | |
| Dissipation factor, 50/60Hz | ASTM D150 | 0.0009 - | |
| Arc resistance, Tungsten{PLC} | ASTM D495 | PLC_7 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/953A-116 |
|---|---|---|---|
| transmittance | 2.54mm | ASTM D1003 | 85 % |
| Haze ratio | 2.54mm | ASTM D1003 | 1 % |
| refractive index | ASTM D542 | 1.586 - |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/953A-116 |
|---|---|---|---|
| UL certification, 94V-0 flame rating | UL 94 | 2.99 mm | |
| UV-light,waterexposure/immersion | UL 746C | F1 - | |
| UL certification, 94V-2 flame rating | UL 94 | 1.47 mm |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/953A-116 |
|---|---|---|---|
| density | 比重 | ASTM D792 | 1.21 - |
| 比重 | ASTM D792 | 1.217 g/cm³ | |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| 平衡,23°C | ASTM D570 | 0.35 % | |
| Specific volume | ASTM D792 | 0.83 cm³/g | |
| Water absorption rate | 平衡,100°C | ASTM D570 | 0.58 % |
| Mold shrinkage flow, 3.2mm | SABICMethod | 0.5-0.7 % | |
| melt mass-flow rate | 300°C/1.2kgf | ASTM D1238 | 7 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/953A-116 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa，6.4mm，未退火，HDT | ASTM D648 | 137 °C |
| Linear coefficient of thermal expansion | -40°C至95°C，流动 | ASTME831 | 6.84E-05 1/°C |
| Heat distortion temperature | 1.82MPa，6.4mm，未退火，HDT | ASTM D648 | 132 °C |
| thermal conductivity | ASTMC177 | 0.19 W/m-°C | |
| Relative temperature index, Mechw/impact | UL 746B | 120 °C | |
| Relative temperature index, Mechw/oimpact | UL 746B | 130 °C | |
| Relative temperature index, Elec | UL 746B | 130 °C | |
| vicat | 速率B/50 | ASTM D1525 | 151 °C |