Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
Ether Neostar™ FN006 Eastman Chemical Company
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Eastman Chemical Company/Neostar™ FN006 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 40 J/m |
| hardness | Test Condition | Test Method | Eastman Chemical Company/Neostar™ FN006 |
|---|---|---|---|
| Shore hardness | 邵氏D,23°C | ASTM D2240 | 55 |
| 邵氏A,23°C | ASTM D2240 | 95 |
| Supplementary Information | Test Condition | Test Method | Eastman Chemical Company/Neostar™ FN006 |
|---|---|---|---|
| tear strength | 23°C | ASTM D1004 | 350 N |
| Mechanical properties | Test Condition | Test Method | Eastman Chemical Company/Neostar™ FN006 |
|---|---|---|---|
| tensile strength | 断裂,23°C,2.00mm4 | ASTM D638 | 22.0 MPa |
| Tensile modulus | 23°C | ASTM D638 | 170 MPa |
| Flexural modulus | 23°C | ASTM D790 | 150 MPa |
| tensile strength | 屈服,23°C,3.00mm,注塑3 | ASTM D638 | 14.0 MPa |
| elongation | 屈服,23°C | ASTM D638 | 38 % |
| 断裂,23°C | ASTM D638 | 400 % |
| elastomer | Test Condition | Test Method | Eastman Chemical Company/Neostar™ FN006 |
|---|---|---|---|
| Kappa modulus | -70°C | ASTM D1043 | 930 MPa |
| -28°C | ASTM D1043 | 240 MPa |
| physical property | Test Condition | Test Method | Eastman Chemical Company/Neostar™ FN006 |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 10 g/10min |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.40 % |
| intrinsic viscosity | 23°C | 内部方法 | 1.2 |
| density | ASTM D792 | 1.13 g/cm³ |
| Thermal performance | Test Condition | Test Method | Eastman Chemical Company/Neostar™ FN006 |
|---|---|---|---|
| Glass Transition Temperature | DSC | -3.00 °C | |
| specific heat | 200°C7 | DSC | 3100 J/kg/°C |
| melting temperature | ASTM D3418 | 205 °C | |
| Fusion temperature | 23°C | ASTME793 | 27.0 kJ/kg |
| specific heat | 100°C6 | DSC | 1800 J/kg/°C |
| Linear coefficient of thermal expansion | MD：23°C | ASTM D696 | 1.5E-04 cm/cm/°C |
| Crystallization peak temperature | DSC | DSC | 140 °C |
| specific heat | 25°C6 | DSC | 1600 J/kg/°C |
| thermal conductivity | 23°C | ASTMC177 | 0.19 W/m/K |
| specific heat | 175°C6 | DSC | 2300 J/kg/°C |
| brittle temperature | ASTM D746 | <-75.0 °C | |
| vicat | ASTM D15255 | 170 °C | |
| specific heat | 150°C6 | DSC | 2000 J/kg/°C |
| 225°C8 | DSC | 2300 J/kg/°C |