PC/ABS 3710-10701 MITSUBISHI ENGINEERING JAPAN
XANTAR™
Shell,Electronic and Electrical Applications
heat-resisting,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/3710-10701 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Multi axis Instrumented Impact Energy | -20°C2 | 内部方法 | 4.00 J |
| 23°C | ISO 6603-2 | 35.0 J | |
| 23°C2 | 内部方法 | 10.0 J |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/3710-10701 |
|---|---|---|---|
| dielectric constant | 1.00GHz | IEC 60250 | 2.80 |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor | 1.00GHz | IEC 60250 | 5E-03 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/3710-10701 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2200 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | >50 % | |
| bending strength | ISO 178 | 80.0 Mpa | |
| Flexural modulus | ISO 178 | 2250 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.0 % |
| tensile strength | 屈服 | ISO 527-2 | 50.0 Mpa |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/3710-10701 |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.60 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.60 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 14.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/3710-10701 |
|---|---|---|---|
| vicat | ISO 306/B50 | 122 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 102 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7E-05 cm/cm/°C |