PC BPL1000-701 SABIC INNOVATIVE NANSHA
LEXAN™ 
Automotive components,Electronic and electrical accessories,Thin walled products
UV resistance,Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/BPL1000-701
Ball Pressure Test75°CIEC 60695-10-2Pass
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af96.1 °C
0.45MPa,Unannealed,3.20mmASTM D648106 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8317E-05 cm/cm/°C
TD：-40to40°CISO 11359-27E-05 cm/cm/°C
TD：-40to40°CASTME8317E-05 cm/cm/°C
MD：-40to40°CISO 11359-27E-05 cm/cm/°C
RTI ElecUL 74680.0 °C
RTI ImpUL 74680.0 °C
RTI StrUL 74680.0 °C
Vicat softening temperature--ISO 306/B120114 °C
--ISO 306/B50113 °C
ASTM D152511111 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/BPL1000-701
Bending modulus50.0mmSpanASTM D7902670 Mpa
ISO 1782370 Mpa
bending strengthYield,50.0mmSpanASTM D790102 Mpa
ISO 17894.8 Mpa
elongationBreakASTM D63896 %
YieldASTM D6384.8 %
Tensile modulusASTM D6382680 Mpa
ISO 527-2/12460 Mpa
Tensile strainBreakISO 527-2/5097 %
YieldISO 527-2/504.7 %
tensile strengthYieldASTM D63863.4 Mpa
YieldISO 527-2/5064.8 Mpa
BreakISO 527-2/5053.5 Mpa
BreakASTM D63851.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/BPL1000-701
Compared to the anti leakage trace indexIEC 60112PLC 3
Dielectric strength1.60mm,inOilASTM D14927 KV/mm
Dissipation factor1MHzIEC 602500.010
50HzIEC 602500.030
60HzIEC 602500.030
Relative permittivity60HzIEC 602503.00
50HzIEC 602503.00
1MHzIEC 602502.90
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/BPL1000-701
melt mass-flow rate300°C/1.2kgASTM D123825 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113323.2 cm3/10min
Shrinkage rateTD：3.20mmInternal Method0.50-0.70 %
MD：3.20mmInternal Method0.50-0.70 %
MD：--2Internal Method0.50-0.70 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Saturation,23°CISO 620.35 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/BPL1000-701
Charpy Notched Impact Strength23°CISO 179/1eA18 kJ/m²
Dart impact23°C,TotalEnergyASTM D376348.6 J
Impact strength of cantilever beam gap-30°CISO 180/1A12 kJ/m²
23°CISO 180/1A18 kJ/m²
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/BPL1000-701
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
Extreme Oxygen IndexISO 4589-236 %
Hot filament ignition temperature1.0mmIEC 60695-2-13800 °C
UL flame retardant rating0.45mmUL 94V-2
0.8mmUL 94V-0