PPO WCD931 BK1006 SABIC INNOVATIVE JAPAN
FLEX NORYL™
Automotive interior parts
High impact resistance,transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE JAPAN/WCD931 BK1006
Shore hardness邵氏A,30秒ASTM D224093
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE JAPAN/WCD931 BK1006
Brittle temperatureASTM D746<-40.0 °C
Hot deformation temperature100°CCCP METHOD10 %
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE JAPAN/WCD931 BK1006
Bending modulusISO 178135 Mpa
100mmSpanASTM D790160 Mpa
elongation断裂2ASTM D638130 %
Break,80°C3CCP METHOD270 %
断裂CCP METHOD310 %
Tensile strain断裂ISO 527-2/50180 %
tensile strength断裂CCP METHOD15.0 Mpa
断裂ISO 527-2/509.00 Mpa
Break,80°C3CCP METHOD15.0 Mpa
断裂2ASTM D6389.00 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE JAPAN/WCD931 BK1006
Compared to the anti leakage trace indexIEC 60112PLC 0
Dielectric constant1MHzASTM D1503.00
Dielectric strength2.00mm,inOilIEC 60243-123 KV/mm
Dissipation factor1MHzASTM D1501E-03
Volume resistivityASTM D2572E+15 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE JAPAN/WCD931 BK1006
melt mass-flow rate250°C/10.0kgASTM D12388.5 g/10min
flammabilityTest ConditionTest MethodSABIC INNOVATIVE JAPAN/WCD931 BK1006
Burning wire flammability index3.0mmIEC 60695-2-12750 °C
Extreme Oxygen IndexISO 4589-229 %
Hot filament ignition temperature3.0mmIEC 60695-2-13775 °C
Smoke densityNon-Flame,0.5mmplaque,Ds,maxASTME662150
Flame,0.5mmplaque,Ds,maxASTME66256
VerticalFlameTestEN50265-2-1PASSES