PC ML-3210ZLP TEIJIN JAPAN
PANLITE®
Casters
Weather resistance,Aging resistance,Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | TEIJIN JAPAN/ML-3210ZLP |
|---|---|---|---|
| Heat Deflection Temperature | TD，HDT | ISO 11359-2 | 0.7 X10-4/℃ |
| 线膨胀系数，MD，HDT | ISO 11359-2 | 0.7 X10-4/℃ | |
| UL flame retardant rating | 1.0mm | UL 94 | V-2 |
| Heat Deflection Temperature | 1.80MPa，HDT | ISO 75-1 | 129 °C |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/ML-3210ZLP |
|---|---|---|---|
| flexural modulus | 2mm/min | ISO 178 | 2400 Mpa |
| tensile strength | 50mm/min，断裂 | ISO 527-1 | 68 Mpa |
| 50mm/min，屈服 | ISO 527-1 | 61 Mpa | |
| Elongation at break | 50mm/min | ISO 527-1 | 105 % |
| bending strength | 2mm/min | ISO 178 | 99 Mpa |
| Impact strength of cantilever beam gap | Notched | ISO 179 | 10 kJ/m² |
| optical performance | Test Condition | Test Method | TEIJIN JAPAN/ML-3210ZLP |
|---|---|---|---|
| Pigment dispersion | 2.0mmt | In-house method | 24 % |
| transmittance | 1.5mmt | JIS K7136 | 80 % |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/ML-3210ZLP |
|---|---|---|---|
| Dissolving fingers | 300℃ | ISO 1133 | 18 cm310min |
| shrinkage rate | TD | In-house method | 0.5-0.7 % |
| MD | In-house method | 0.5-0.7 % |