Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LLDPE PRE-ELEC® PE 1271 Premix Oy
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | Premix Oy/PRE-ELEC® PE 1271 |
|---|---|---|---|
| Inflation ratio (BUR) | >1.80 | ||
| Blow molding machine barrel temperature | 160to200 °C |
| Mechanical properties | Test Condition | Test Method | Premix Oy/PRE-ELEC® PE 1271 |
|---|---|---|---|
| elongation | 横向流量:屈服 | ASTM D638 | 17 % |
| Tensile strain | Break,0.300mm3 | ISO 527-2 | 590 % |
| tensile strength | --2 | ISO 527-2 | 22.0 MPa |
| elongation | 流量:屈服 | ASTM D638 | 13 % |
| Tensile strain | Break,0.300mm4 | ISO 527-2 | 600 % |
| tensile strength | 横向流量 | ASTM D638 | 22.1 MPa |
| Tensile strain | 流量:屈服 | ISO 527-2 | 13 % |
| tensile strength | 流量:屈服 | ISO 527-2 | 21.0 MPa |
| 横向流量:屈服 | ISO 527-2 | 15.0 MPa | |
| 0.400mm3 | ISO 527-2 | 24.0 MPa | |
| elongation | 断裂 | ASTM D638 | 600 % |
| 流量:断裂 | ASTM D638 | 590 % | |
| tensile strength | 横向流量:屈服 | ASTM D638 | 15.2 MPa |
| 流量:屈服 | ASTM D638 | 21.4 MPa | |
| Tensile strain | 横向流量:屈服 | ISO 527-2 | 17 % |
| tensile strength | 流量 | ASTM D638 | 24.1 MPa |
| Electrical performance | Test Condition | Test Method | Premix Oy/PRE-ELEC® PE 1271 |
|---|---|---|---|
| Surface Resistivity | ESDSTM11.11 | <1.0E+5 ohms | |
| IEC 61340-2-3 | <1.0E+5 ohms |
| physical property | Test Condition | Test Method | Premix Oy/PRE-ELEC® PE 1271 |
|---|---|---|---|
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 1.7 g/10min |
| density | ASTM D792 | 1.02 g/cm³ | |
| ISO 1183 | 1.02 g/cm³ | ||
| melt mass-flow rate | 190°C/21.6kg | ISO 1133 | 35 g/10min |
Contact Us
Get App