Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT B 4300 K4 BASF GERMANY
Ultradur®
Engineering accessories,Shell,electrical machinery,printed circuit board
High rigidity,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B 4300 K4 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 35 kJ/m² |
| -30°C | ISO 179/1eU | 26 kJ/m² |
| hardness | Test Condition | Test Method | BASF GERMANY/B 4300 K4 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 150 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B 4300 K4 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 0.012 |
| relative permittivity | 100Hz | IEC 60250 | 4.00 |
| 1MHz | IEC 60250 | 3.70 | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | PLC 4 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.019 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B 4300 K4 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3500 Mpa | |
| bending strength | ISO 178 | 100 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 6.0 % |
| Flexural modulus | ISO 178 | 3400 Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1300 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 48.0 Mpa |
| flammability | Test Condition | Test Method | BASF GERMANY/B 4300 K4 |
|---|---|---|---|
| Flammability level | 1.6mm | IEC 60695-11-10,-20 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/B 4300 K4 |
|---|---|---|---|
| Apparent density | 0.70to0.80 g/cm³ | ||
| Shrinkage rate | TD | ISO 294-4 | 1.9 % |
| viscosity number | ISO 307 | 115 cm³/g | |
| Shrinkage rate | MD | ISO 294-4 | 1.9 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 16.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B 4300 K4 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 223 °C | |
| thermal conductivity | DIN 52612 | 0.27 W/m/K | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 170 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 70.0 °C | |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 8.0E-5到9.0E-5 cm/cm/°C |
| specific heat | 1150 J/kg/°C |