PA66/6 G33NC201 KUAZOT SHANGHAI
VOLGAMID®
Automotive sector、Electronic field、Electrical field
Glass fiber reinforced、enhance、33% glass fiber reinforce、Granular
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | KUAZOT SHANGHAI/G33NC201 |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.3 / 0.8 | |
| Water absorption rate | ISO 62 | -- % | |
| ash content | ISO 3451-4 | 33±2 | |
| density | ISO 1183 | 1.38 g/cm³ |
| Mechanical properties | Test Condition | Test Method | KUAZOT SHANGHAI/G33NC201 |
|---|---|---|---|
| tensile strength | ISO 527 | 209 Mpa | |
| Impact strength of simply supported beam without notch | ISO 179 | NB kJ/m² | |
| Charpy Notched Impact Strength | ISO 179 | 16.5 kJ/m² | |
| Rockwell hardness | ISO 2039/2 | 120 | |
| elongation | 断裂 | ISO 527 | -- % |
| bending strength | 4.55 | 296 Mpa | |
| Flexural modulus | 4.55 | 9900 Mpa |
| Electrical performance | Test Condition | Test Method | KUAZOT SHANGHAI/G33NC201 |
|---|---|---|---|
| Surface Resistivity | IEC 93 | 10^15 Ω | |
| dielectric strength | IEC 60243-3 | 27.5 KV/mm | |
| Volume resistivity | IEC 93 | 10^16 Ω·cm |
| Thermal performance | Test Condition | Test Method | KUAZOT SHANGHAI/G33NC201 |
|---|---|---|---|
| Heat distortion temperature | 1.81Mpa，HDT | ISO 75 | 244 °C |
| UL Vertical Combustion | UL -94 | HB |