Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM F10-02 MITSUBISHI THAILAND
Iupital™
Automotive sector
wear resistant、Low temperature resistanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI THAILAND/F10-02 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 7.0 kJ/m² |
| -30°C | ISO179/1eA | 6.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI THAILAND/F10-02 |
|---|---|---|---|
| Tensile stress | ISO527-2 | 63.0 Mpa | |
| Bending stress | ISO178 | 83.0 Mpa | |
| Tensile strain | 屈服 | ISO527-2 | 10 % |
| Tensile modulus | ISO527-2 | 2600 Mpa | |
| Flexural modulus | ISO178 | 2400 Mpa | |
| Tensile strain | 断裂 | ISO527-2 | 40 % |
| Electrical performance | Test Condition | Test Method | MITSUBISHI THAILAND/F10-02 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+16 ohms | |
| Volume resistivity | IEC60093 | 1E+14 ohms·cm | |
| dielectric strength | IEC60243-1 | 19 KV/mm |
| flammability | Test Condition | Test Method | MITSUBISHI THAILAND/F10-02 |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| physical property | Test Condition | Test Method | MITSUBISHI THAILAND/F10-02 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.20 % |
| melt mass-flow rate | 190°C/2.16kg | ISO1133 | 3.0 g/10min |
| Shrinkage rate | MD：3.00mm | 内部方法 | 2.2 % |
| density | ISO1183 | 1.41 g/cm³ |
| Thermal performance | Test Condition | Test Method | MITSUBISHI THAILAND/F10-02 |
|---|---|---|---|
| 1.8MPa,未退火 | ISO75-2/A | 96.0 °C | |
| melting temperature | ISO11357-3 | 165 °C | |
| MD | ISO11359-2 | 1.2E-04 cm/cm/°C |