PBT LW9020 BK580 DUPONT USA
Cristin®
Electronic and electrical、Automotive Applications、Industrial applications
Low warpage、Flame retardant、Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/LW9020 BK580 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/LW9020 BK580 |
|---|---|---|---|
| Odor | VDA270 | 3.50 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/LW9020 BK580 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 160 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 7000 Mpa | |
| Flexural modulus | ASTM D790/ISO 178 | 6200 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 160 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.5 % |
| Flexural modulus | ISO 178 | 6200 Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 7000 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 断裂 | ISO 527-2 | 108 Mpa |
| other | Test Condition | Test Method | DUPONT USA/LW9020 BK580 |
|---|---|---|---|
| characteristic | 可加工性良好 耐化学性良好 | ||
| purpose | 工业领域 汽车领域的应用 |
| Physical properties | Test Condition | Test Method | DUPONT USA/LW9020 BK580 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.35 |
| flammability | Test Condition | Test Method | DUPONT USA/LW9020 BK580 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94,IEC60695-11-10,-20 | HB |
| burning rate | 1.00mm | ISO 3795 | 38 mm/min |
| Thermal performance | Test Condition | Test Method | DUPONT USA/LW9020 BK580 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| melting temperature | ISO 11357-3 | 225 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 205 °C |
| 1.8MPa,退火，HDT | ISO 75-2/A | 180 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 150 °C |