POM S1320-0021 BASF GERMANY
Ultraform®
Automotive Applications、Toy
High impact resistance、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/S1320-0021 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.5 kJ/m² |
| -30°C | ISO 179/1eA | 5.5 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 170 kJ/m² |
| -30°C | ISO 179/1eU | 170 kJ/m² |
| hardness | Test Condition | Test Method | BASF GERMANY/S1320-0021 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 155 Mpa |
| Supplementary Information | Test Condition | Test Method | BASF GERMANY/S1320-0021 |
|---|---|---|---|
| ISOType | ISO 9988-1 | POM-K.M-GNR.04-002 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/S1320-0021 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3000 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 66.0 Mpa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1450 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 9.0 % |
| Nominal tensile fracture strain | ISO 527-2/50 | 30 % |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/S1320-0021 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 85 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| relative permittivity | 1MHz | IEC 60250 | 3.70 |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 5E-03 |
| flammability | Test Condition | Test Method | BASF GERMANY/S1320-0021 |
|---|---|---|---|
| Flammability level | 1.6mm | IEC 60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/S1320-0021 |
|---|---|---|---|
| Apparent density | 0.85 g/cm³ | ||
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 11.0 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 2.1 % |
| MD | ISO 294-4 | 2.1 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.80 % | |
| density | ISO 1183 | 1.41 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/S1320-0021 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 171 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C |
| maximum service temperature | 短周期操作 | 100 °C |