Unspecified PP School 20.1 Poly Plastic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Poly Plastic/PP School 20.1 |
|---|---|---|---|
| Charpy Notched Impact Strength | 20°C | 8.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 20°C | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Poly Plastic/PP School 20.1 |
|---|---|---|---|
| Flexural modulus | 23°C | 1300 MPa | |
| Tensile strain | 断裂 | 13 % | |
| bending strength | 25.0 MPa | ||
| tensile strength | 屈服 | 25.0 MPa |
| Electrical performance | Test Condition | Test Method | Poly Plastic/PP School 20.1 |
|---|---|---|---|
| Volume resistivity | 1E+15 ohms·cm |
| physical property | Test Condition | Test Method | Poly Plastic/PP School 20.1 |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | 3.6 g/10min | |
| Shrinkage rate | 1.2to1.5 % | ||
| density | 1.04 g/cm³ |
| Thermal performance | Test Condition | Test Method | Poly Plastic/PP School 20.1 |
|---|---|---|---|
| Heat distortion temperature | 线形热膨胀系数-流动(-20到110°C)，HDT | 7E-06 cm/cm/°C | |
| 熔融温度，HDT | 162 °C | ||
| 0.45MPa,未退火，HDT | 110 °C | ||
| 1.8MPa,未退火，HDT | 80.0 °C |