Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO SE1-701 BK SABIC INNOVATIVE US
NORYL™
Automotive components、Household appliances
High temperature resistan、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/SE1-701 BK |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 49.7 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/SE1-701 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2670 Mpa | |
| bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 100 Mpa |
| elongation | 屈服 | ASTM D638 | 4.0 % |
| Flexural modulus | 50.0mm跨距5 | ASTM D790 | 2700 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.3 % |
| tensile strength | 断裂 | ISO 527-2/50 | 50.8 Mpa |
| 屈服 | ISO 527-2/50 | 61.3 Mpa | |
| Tensile modulus | ASTM D638 | 2500 Mpa | |
| elongation | 断裂 | ASTM D638 | 15 % |
| tensile strength | Break | ASTM D638 | 53.1 Mpa |
| Flexural modulus | 100mmSpan6 | ASTM D790 | 2400 Mpa |
| bending strength | ISO 178 | 99.5 Mpa | |
| Flexural modulus | ISO 178 | 2560 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 65.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 21 % |
| bending strength | Yield,100mmSpan6 | ASTM D790 | 98.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/SE1-701 BK |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 3.4E-03 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| Dissipation Factor | 60Hz | ASTM D150 | 3.4E-03 |
| dielectric constant | 60Hz | ASTM D150 | 2.52 |
| Volume resistivity | ASTM D257 | 2.3E+16 ohms·cm | |
| dielectric constant | 50Hz | ASTM D150 | 2.52 |
| dielectric strength | 3.20mm,inOil | ASTM D149 | 18 KV/mm |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | ASTM D150 | 2.1E-03 |
| dielectric constant | 1MHz | ASTM D150 | 2.46 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/SE1-701 BK |
|---|---|---|---|
| UL flame retardant rating | RadiantPanelListing(UL) | UL 94 | RP100 |
| 6.0mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/SE1-701 BK |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| TD2 | 内部方法 | 0.50-0.70 % | |
| Water absorption rate | 24hr | ASTM D570 | 0.060 % |
| Outdoor applicability | UL 746C | f1 | |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 8.5 g/10min |
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 8.70 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/SE1-701 BK |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Be | 129 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 118 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 127 °C |
| 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 129 °C | |
| 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 115 °C | |
| RTI Str | UL 746 | 110 °C | |
| vicat | -- | ISO 306/B120 | 135 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 8.8E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 132 °C |
| RTI Imp | UL 746 | 105 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 113 °C |
| RTI Elec | UL 746 | 110 °C |