Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A 20 V35 TECNICA ITALY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TECNICA ITALY/A 20 V35 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| -30°C | ISO 179/1eU | 55 kJ/m² |
| Mechanical properties | Test Condition | Test Method | TECNICA ITALY/A 20 V35 |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1A | 12500 Mpa |
| Tensile strain | 断裂, 23°C | ISO 527-2 | 2.1 % |
| bending strength | 23°C | ISO 178 | 260 Mpa |
| Flexural modulus | 23°C | ISO 178 | 11000 Mpa |
| tensile strength | 断裂, 23°C | ISO 527-2/1A | 175 Mpa |
| Electrical performance | Test Condition | Test Method | TECNICA ITALY/A 20 V35 |
|---|---|---|---|
| relative permittivity | IEC 60250 | 3.40 | |
| Dissipation Factor | IEC 60250 | 0.020 | |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| dielectric strength | 0.800 mm | IEC 60243-1 | 32 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 1 |
| Surface Resistivity | IEC 60093 | 1.0E+14 ohms |
| flammability | Test Condition | Test Method | TECNICA ITALY/A 20 V35 |
|---|---|---|---|
| UL flame retardant rating | 3.2 mm | UL 94 | V-0 |
| Burning wire flammability index | 0.8 mm | IEC 60695-2-12 | 960 °C |
| 3.2 mm | IEC 60695-2-12 | 960 °C | |
| UL flame retardant rating | 0.8 mm | UL 94 | V-0 |
| 1.6 mm | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 31 % | |
| Burning wire flammability index | 1.6 mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.6 mm | IEC 60695-2-13 | 725 °C |
| physical property | Test Condition | Test Method | TECNICA ITALY/A 20 V35 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.7 % |
| 24 hr, 23°C | ISO 62 | 0.60 % |
| Thermal performance | Test Condition | Test Method | TECNICA ITALY/A 20 V35 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 263 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/Af | 244 °C |
| injection | Test Condition | Test Method | TECNICA ITALY/A 20 V35 |
|---|---|---|---|
| Suggested maximum moisture content | 0.20 % | ||
| Temperature in the middle of the barrel | 270 to 280 °C | ||
| Temperature at the rear of the barrel | 265 to 275 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 280 to 290 °C | ||
| Temperature | 60 to 90 °C |