PEI 2410-7301 SABIC INNOVATIVE US
ULTEM™
Automotive Applications、Electrical applications
Thermal stability、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/2410-7301 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 114 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/2410-7301 |
|---|---|---|---|
| Flexural modulus | 100mmSpan | ASTM D790 | 11700 Mpa |
| Tensile modulus | ASTM D638 | 11700 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.5 % |
| bending strength | Break,100mmSpan | ASTM D790 | 241 Mpa |
| tensile strength | 断裂 | ASTM D638 | 179 Mpa |
| 屈服 | ASTM D638 | 186 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/2410-7301 |
|---|---|---|---|
| Dissipation Factor | 1kHz | ASTM D150 | 2E-03 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| dielectric strength | 1.60mm,inOil | ASTM D149 | 24 KV/mm |
| Volume resistivity | ASTM D257 | 1.5E+16 ohms·cm | |
| dielectric constant | 1kHz | ASTM D150 | 3.70 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 5 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/2410-7301 |
|---|---|---|---|
| UL flame retardant rating | 0.25mm | UL 94 | V-0 |
| NBSSmokeDensity-Flaming,Ds,4min | ASTME662 | 1.00 | |
| UL flame retardant rating | 1.5mm | UL 94 | 5VA |
| Limiting Oxygen Index | ASTM D2863 | 54 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/2410-7301 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.10-0.30 % |
| Water absorption rate | 24hr | ASTM D570 | 0.13 % |
| 平衡,23°C | ASTM D570 | 0.90 % | |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 5.2 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/2410-7301 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 213 °C |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 1.4E-05 cm/cm/°C |
| vicat | ASTM D15255 | 234 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 216 °C |
| RTI Imp | UL 746 | 170 °C | |
| RTI Str | UL 746 | 170 °C | |
| RTI Elec | UL 746 | 170 °C |