PPA AS-1945HS SOLVAY USA
AMODEL®
Metal substitution、Industrial applications、Parts under the hood of a、Machine/mechanical compon、Thick wall accessories (c、Valves/valve components、Power/Other Tools、Application in the automo、Shell、Industrial components
Filler: Glass fiber reinf、45% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/AS-1945HS |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 15100 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.5 % |
| Tensile modulus | --4 | ASTM D638 | 10300 Mpa |
| bending strength | 屈服 | ASTM D790 | 359 Mpa |
| Tensile modulus | -- | ASTM D638 | 15200 Mpa |
| bending strength | ISO 178 | 335 Mpa | |
| Flexural modulus | ISO 178 | 12600 Mpa | |
| tensile strength | 断裂4 | ASTM D638 | 107 Mpa |
| 断裂 | ISO 527-2 | 244 Mpa | |
| 断裂 | ASTM D638 | 252 Mpa | |
| Flexural modulus | ASTM D790 | 13800 Mpa |
| physical property | Test Condition | Test Method | SOLVAY USA/AS-1945HS |
|---|---|---|---|
| Shrinkage rate | TD3 | ASTM D955 | 0.60 % |
| TD | ISO 294-4 | 0.60 % | |
| MD | ISO 294-4 | 0.20 % | |
| MD3 | ASTM D955 | 0.20 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/AS-1945HS |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 282 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/Af | 282 °C | |
| melting temperature | ISO 11357-3 | 312 °C |