Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA HRA222-WH4C030U SABIC INNOVATIVE US
GELOY™
Electrical appliances、Electronic field、Electrical field
UV resistance、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HRA222-WH4C030U |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 Mpa |
| Bending stress 6, 7 | ISO 178 | 93.0 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 51.0 Mpa |
| elongation | 屈服 5 | ASTM D638 | 4.2 % |
| 屈服 4 | ASTM D638 | 4.3 % | |
| 屈服 | ISO 527-2/5 | 4.3 % | |
| 断裂 | ISO 527-2/5, ISO 527-2/50 | > 50 % | |
| Tensile modulus | -- 3 | ASTM D638 | 2590 Mpa |
| tensile strength | 屈服 4 | ASTM D638 | 63.0 Mpa |
| 屈服 5 | ASTM D638 | 59.0 Mpa | |
| 断裂 | ISO 527-2/50 | 45.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 4.4 % |
| Bending modulus 6 | ISO 178 | 2510 Mpa | |
| tensile strength | 断裂 4 | ASTM D638 | 56.0 Mpa |
| 屈服 | ISO 527-2/5 | 62.0 Mpa | |
| 断裂 5 | ASTM D638 | 66.0 Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 2520 Mpa |
| elongation | 断裂 5 | ASTM D638 | > 100 % |
| 断裂 4 | ASTM D638 | > 100 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HRA222-WH4C030U |
|---|---|---|---|
| CTI | IEC 60112 | 600 V | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HRA222-WH4C030U |
|---|---|---|---|
| UL flame retardant rating | 2.3 mm | UL 94 | 5VB |
| 2.0 mm | UL 94 | V-0 | |
| 0.8 mm | UL 94 | V-2 | |
| Limiting Oxygen Index | ISO 4589-2 | 29 % | |
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 2.3 mm, Testing by SABIC | UL 94 | 5VB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HRA222-WH4C030U |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.20 % |
| Outdoor applicability | UL 746C | f1 | |
| Shrinkage rate - Flow 2 | 内部方法 | 0.40 到 0.60 % | |
| Molten Volume Flow Rate (MVR) | 260°C/2.16 kg | ISO 1133 | 13.0 cm3/10min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HRA222-WH4C030U |
|---|---|---|---|
| -- | ISO 306/A50 | 111 °C | |
| Hot deformation temperature 10 | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Ae | 88.0 °C |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.5E-5 cm/cm/°C | |
| -- | ISO 306/B50 | 102 °C | |
| 横向 : -30 到 80°C | ISO 11359-2 | 7.1E-5 cm/cm/°C | |
| RTI Imp | UL 746 | 90.0 °C | |
| -- | ISO 306/B120 | 104 °C | |
| 流动 : -30 到 80°C | ISO 11359-2 | 6.9E-5 cm/cm/°C | |
| RTI | UL 746 | 90.0 °C | |
| Ball Pressure Test | 73 到 77°C | IEC 60695-10-2 | 通过 |
| Hot deformation temperature 10 | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Be | 99.0 °C |
| RTI Elec | UL 746 | 90.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/HRA222-WH4C030U |
|---|---|---|---|
| Temperature | 50 到 70 °C | ||
| Temperature at the rear of the barrel | 200 到 230 °C | ||
| Processing (melt) temperature | 230 到 270 °C | ||
| 220 到 260 °C | |||
| drying temperature | 80 到 90 °C | ||
| Temperature at the front of the material cylinder | 230 到 270 °C | ||
| drying time | 2.0 到 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Hopper temperature | 60 到 80 °C | ||
| Temperature in the middle of the barrel | 220 到 260 °C |
Contact Us
Get App