Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 100ST-BK010 DUPONT USA
Delrin®
Automotive sector、Construction field
High impact resistance、wear resistant、Toughening
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/100ST-BK010 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 90 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 18 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 90 kJ/m² |
| -40°C | ISO 180/1A | 20 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/100ST-BK010 |
|---|---|---|---|
| Emission | VDA275 | <8.00 mg/kg | |
| SpecificWear | ASTM D1894 | 60.0 10^-6mm³/N·m | |
| Emissions of Organic Compounds | VDA277 | 2.90 µgC/g |
| hardness | Test Condition | Test Method | DUPONT USA/100ST-BK010 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 105 |
| M计秤 | ISO 2039-2 | 58 |
| Electrical performance | Test Condition | Test Method | DUPONT USA/100ST-BK010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 4.40 |
| 1MHz | IEC 60250 | 3.80 | |
| Surface Resistivity | IEC 60093 | 1E+14 ohms |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/100ST-BK010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 1400 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | 1100 Mpa |
| Nominal tensile fracture strain | ISO 527-2 | >50 % | |
| Flexural modulus | ISO 178 | 1100 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 30 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 550 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 41.0 Mpa |
| bending strength | 3.5%应变 | ISO 178 | 34.0 Mpa |
| coefficient of friction | vs.Itself-Dynamic,1hr | ASTM D1894 | 0.32 |
| flammability | Test Condition | Test Method | DUPONT USA/100ST-BK010 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| burning rate | 1.00mm | ISO 3795 | 41 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/100ST-BK010 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 1.70 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.4 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.90 % |
| Shrinkage rate | MD | ISO 294-4 | 1.3 % |
| MediumDensity | 1.14 g/cm³ | ||
| melt mass-flow rate | ISO 1133 | 2.0 g/10min | |
| density | ISO 1183 | 1.34 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.35 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/100ST-BK010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 178 °C | |
| AnnealingTemperature | 160 °C | ||
| Effective thermal diffusivity coefficient | 6E-08 m²/s | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 100 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 60.0 °C | |
| AnnealingTime-Optional | 30.0 min/mm | ||
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.4E-04 cm/cm/°C | |
| Glass Transition Temperature | ISO 11357-2 | -35.0 °C |