ABS EXCELLOY CK10P Techno Polymer Co, Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Techno Polymer Co, Ltd./EXCELLOY CK10P |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 50 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 490 J/m |
| hardness | Test Condition | Test Method | Techno Polymer Co, Ltd./EXCELLOY CK10P |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 106 |
| R级 | ASTM D785 | 108 |
| Mechanical properties | Test Condition | Test Method | Techno Polymer Co, Ltd./EXCELLOY CK10P |
|---|---|---|---|
| bending strength | -- | ASTM D790 | 78.5 MPa |
| Flexural modulus | -- | ISO 178 | 1800 MPa |
| tensile strength | 屈服 | ASTM D638 | 49.0 MPa |
| 屈服 | ISO 527-2 | 45.0 MPa | |
| bending strength | -- | ISO 178 | 67.0 MPa |
| Flexural modulus | -- | ASTM D790 | 2260 MPa |
| physical property | Test Condition | Test Method | Techno Polymer Co, Ltd./EXCELLOY CK10P |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.40to0.60 % | |
| density | ISO 1183 | 1.10 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | Techno Polymer Co, Ltd./EXCELLOY CK10P |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 105 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 94.0 °C |