Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC BX7241-BR6G159 SABIC INNOVATIVE NANSHA
LEXAN™
Plastic bag、Lighting applications、Thin walled components
Low temperature resistanc、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/BX7241-BR6G159 |
|---|---|---|---|
| 0°C | ASTM D256 | 420 J/m | |
| 23°C | ISO 180/1A | 28 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 60.0 J |
| 23°C | ASTM D256 | 690 J/m | |
| -30°C | ASTM D256 | 190 J/m | |
| ISO 180/1A | 11 kJ/m² | ||
| 0°C | ISO 180/1A | 11 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/BX7241-BR6G159 |
|---|---|---|---|
| yield | ASTM D638 | 67.0 Mpa | |
| ASTM D638 | 4.4 % | ||
| ISO 527-2/50 | 62.0 Mpa | ||
| Yield, 50.0mm span | ASTM D790 | 107 Mpa | |
| fracture | ISO 527-2/50 | 45.0 Mpa | |
| ASTM D638 | 65.0 Mpa | ||
| ISO 527-2/50 | 90 % | ||
| ASTM D638 | 120 % | ||
| yield | ISO 527-2/50 | 4.2 % | |
| --9 | ISO 178 | 99.0 Mpa | |
| --8 | ISO 178 | 98.0 Mpa | |
| 50.0mm span | ASTM D790 | 2450 Mpa | |
| --1 | ASTM D638 | 2500 Mpa | |
| --7 | ISO 178 | 2600 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 105 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/BX7241-BR6G159 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+16 ohms·cm | |
| Surface Resistivity | ASTM D257 | >2.0E+15 ohms | |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 4 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/BX7241-BR6G159 |
|---|---|---|---|
| Hot filament ignition temperature | 1.50mm | IEC 60695-2-13 | 825 °C |
| UL flame retardant rating | 3.00mm | UL 94 | 5VA |
| 0.600mm | UL 94 | V-0 | |
| Burning wire flammability index | 0.750mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.00mm | IEC 60695-2-13 | 825 °C |
| 1.00mm | IEC 60695-2-13 | 800 °C | |
| UL flame retardant rating | 0.500mm | UL 94 | V-1 |
| 1.50mm | UL 94 | 5VB | |
| 0.200mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/BX7241-BR6G159 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.60 % |
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 18 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 18.0 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/BX7241-BR6G159 |
|---|---|---|---|
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 5.9E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 103 °C |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 80.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 93.0 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 5.9E-05 cm/cm/°C |
| RTI Elec | UL 746 | 80.0 °C |