Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LGK5030 SABIC INNOVATIVE JAPAN
LEXAN™
Electronic and electrical、Home appliance accessorie、Automotive components
High temperature resistan、Flame retardant、Filler: Glass fiber reinf
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/LGK5030 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 120 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/LGK5030 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 4.0 % |
| tensile strength | 断裂 | ASTM D638 | 142 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 10700 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 187 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/LGK5030 |
|---|---|---|---|
| dielectric strength | 3.20mm,inOil | ASTM D149 | 16 KV/mm |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/LGK5030 |
|---|---|---|---|
| UL flame retardant rating | 1.47mm | UL 94 | V-1 |
| 3.61mm | UL 94 | 5VA | |
| 2.79mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/LGK5030 |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 0.14 % |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.050-0.25 % |
| density | ASTM D792 | 1.61 g/cm³ | |
| Shrinkage rate | TD:3.20mm | 内部方法 | 0.10-0.30 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/LGK5030 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 144 °C |
| Linear coefficient of thermal expansion | MD:-30到30°C | ASTM D696 | 2.2E-05 cm/cm/°C |
| TD:-30到30°C | ASTM D696 | 4E-05 cm/cm/°C |