PBT 1101G-30 TORAY JAPAN
Toraycon®
Automotive sector、Electronic field、Electrical field
Glass fiber reinforced、Flame retardant、High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Burning Rate | UL94 | HB | |
| Linear thermal expansion coefficient | MD：-30到100°C | ISO11359-2 | 4.1E-05 cm/cm/°C |
| 0.45MPa, Unannealed | ISO75-2/B | 220 °C | |
| 1.8MPa, Unannealed | ISO75-2/A | 213 °C | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 2.0x10^-5 mm/mm.℃ | |
| Heat Deflection Temperature | ASTM D648/ISO 75 | 217 ℃（℉） |
| Hardness | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Rockwell Hardness | M计秤,23°C | ISO2039-2 | 90 |
| Additional | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| 250°C,1.00mm | 内部方法 | 9.60 CM |
| Physical | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Modeling Shrinkage | TD:3.00mm1 | 内部方法 | 1.0 % |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.070 % |
| Modeling Shrinkage | MD:3.00mm2 | 内部方法 | 0.30 % |
| Mechanical Properties | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Flexural Strength | ASTM D790/ISO 178 | 195 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 5 % | |
| Rockwell Hardness | ASTM D785 | M91 | |
| Tensile Strength | ASTM D638/ISO 527 | 145 kg/cm²(MPa)[Lb/in²] | |
| Tensile Modulus | 23°C | ISO527-2 | 10200 Mpa |
| Tensile Stress | 145 Mpa | ||
| Flexural Stress | ISO178 | 220 Mpa | |
| Coefficient of Friction (vs.Metal) | SuzukiMethod | 0.150 | |
| Tensile Strain | 断裂,23°C | ISO527-2 | 2.5 % |
| Flexural Modulus | 23°C | ISO178 | 9600 Mpa |
| Izod notch impact strength | ASTM D256/ISO 179 | 35 kg·cm/cm(J/M)ft·lb/in | |
| Flexural Modulus | ASTM D790/ISO 178 | 8800 kg/cm²(MPa)[Lb/in²] | |
| Coefficient of Friction | 0.19 |
| Other | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| characteristic | 30%玻璃纤维增强级，标准型号 |
| Impact Properties | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 45 kJ/m² |
| Physical Properties | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.07 % | |
| Density | ASTM D792/ISO 1183 | 1.55 |
| Flammability | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Flame Rating | 0.794mm | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Dielectric Constant | 23°C,1kHz | IEC60250 | 4.20 |
| Dielectric Strength | IEC60243-1 | 36 KV/mm | |
| Arc Resistance | IEC60950 | 120 sec | |
| Volume Resistivity | IEC60093 | 5E+16 ohms·cm | |
| Dielectric Constant | 23°C,50Hz | IEC60250 | 3.70 |
| Dissipation Factor? | 2E-03 | ||
| 23°C,1MHz | 0.020 | ||
| Volume Resistivity | ASTM D257/IEC 60093 | 2.5x10^14 Ω.cm | |
| Comparative Tracking Index | CTI | UL746 | PLC 2 |