Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PARA 1022 SOLVAY USA
IXEF®
Vehicle electronics、Automotive interior parts
high strength、Creep resistance、50%、glass fibre
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/1022 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 850 J/m |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/1022 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 20000 Mpa | |
| bending strength | ISO 178 | 400 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.9 % |
| Flexural modulus | ISO 178 | 19000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 280 Mpa |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/1022 |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | 0.017 | |
| dielectric strength | IEC 60243-1 | 31 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| dielectric constant | 110Hz | IEC 60250 | 4.60 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | SOLVAY USA/1022 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 25 % |
| physical property | Test Condition | Test Method | SOLVAY USA/1022 |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.10-0.30 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.16 % |
| Water absorption - Ejil, 65% RH | 内部方法 | 1.50 | |
| density | ISO 1183 | 1.64 g/cm³ |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/1022 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 230 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.5E-05 cm/cm/°C |