PA6 A1025 UNITIKA JAPAN
--
Electrical enclosure、Application in the automo、Parts under the hood of a、Vehicle electronics、Architectural application
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UNITIKA JAPAN/A1025 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | kJ/m² | 35 51 |
| hardness | Test Condition | Test Method | UNITIKA JAPAN/A1025 |
|---|---|---|---|
| Rockwell hardness | R计秤 | 116 97 |
| Mechanical properties | Test Condition | Test Method | UNITIKA JAPAN/A1025 |
|---|---|---|---|
| Tensile modulus | MPa | 3100 1800 | |
| Bending stress | MPa | 110 60.0 | |
| Tensile strain | 断裂 | % | 3.4 4.0 |
| Flexural modulus | MPa | 3000 1500 | |
| Tensile stress | 断裂 | MPa | 77.0 41.0 |
| Electrical performance | Test Condition | Test Method | UNITIKA JAPAN/A1025 |
|---|---|---|---|
| dielectric constant | 1MHz | 3.00 -- | |
| dielectric strength | 1.00mm | kV/mm | 25 -- |
| Dissipation Factor | 1MHz | 0.010 -- | |
| Volume resistivity | ohms·cm | 1E+16 -- |
| flammability | Test Condition | Test Method | UNITIKA JAPAN/A1025 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | V-0 V-0 |
| physical property | Test Condition | Test Method | UNITIKA JAPAN/A1025 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | % | 1.5 1.5 |
| Water absorption rate | 平衡,23°C,50%RH | % | 1.9 1.9 |
| 23°C,24hr | % | 1.2 1.2 | |
| Shrinkage rate | MD:3.20mm | % | 1.1 1.1 |
| Thermal performance | Test Condition | Test Method | UNITIKA JAPAN/A1025 |
|---|---|---|---|
| 1.8MPa,未退火 | °C | 66.0 -- | |
| 0.45MPa,未退火 | °C | 170 -- | |
| MD | cm/cm/°C | 1E-04 1E-04 |