TPEE KP3355 KOLON KOREA
KOPEL®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | KOLON KOREA/KP3355 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 55 |
| 邵氏D | ISO 868 | 55 |
| Supplementary Information | Test Condition | Test Method | KOLON KOREA/KP3355 |
|---|---|---|---|
| Resilience | 50 % |
| Mechanical properties | Test Condition | Test Method | KOLON KOREA/KP3355 |
|---|---|---|---|
| elongation at break | ASTM D412/ISO 527 | 650 % | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 700 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 33.0 Mpa |
| ASTM D412/ISO 527 | 360 kg/cm²(MPa)[Lb/in²] | ||
| Flexural modulus | 23°C | ISO 178 | 146 Mpa |
| Taber wear resistance | 1000Cycles,CS-17Wheel | ASTM D1044 | 5.00 mg |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | NB kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | 屈服,23°C | ASTM D638 | 30.9 Mpa |
| elongation | 屈服,23°C | ASTM D638 | 770 % |
| Flexural modulus | 23°C | ASTM D790 | 211 Mpa |
| Electrical performance | Test Condition | Test Method | KOLON KOREA/KP3355 |
|---|---|---|---|
| Dissipation Factor | ASTM D150 | 6E-04 | |
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric constant | ASTM D150 | 4.70 |
| Physical properties | Test Condition | Test Method | KOLON KOREA/KP3355 |
|---|---|---|---|
| density | ASTM D955 | 1.19 % | |
| Shrinkage rate | ASTM D955 | 1.1-1.3 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 18 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.5 % |
| flammability | Test Condition | Test Method | KOLON KOREA/KP3355 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | KOLON KOREA/KP3355 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.4 % |
| MD | ASTM D955 | 1.2 % | |
| MD | ISO 294-4 | 1.3 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.62 % |
| melt mass-flow rate | 220°C/2.16kg | ASTM D1238 | 25 g/10min |
| 220°C/2.16kg | ISO 1133 | 28 g/10min | |
| Water absorption rate | 平衡,23°C,60%RH | ASTM D570 | 0.50 % |
| Thermal performance | Test Condition | Test Method | KOLON KOREA/KP3355 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB（1.5mm) | |
| vicat | ISO 306/A50 | 170 °C | |
| melting temperature | ISO 11357-3 | 200 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 102 °C |
| brittle temperature | ASTM D746 | <-70.0 °C | |
| melting temperature | ASTM D3418 | 200 °C | |
| 200 ℃（℉） |