PBT TS550G6A Nature 浙江新力
--
--
电子电器部件
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | 浙江新力/TS550G6A Nature |
|---|---|---|---|
| Yield bending strength | ISO178 | 200 Mpa | |
| Tensile strength at break | ISO527 | 125 Mpa | |
| Flexural modulus | ISO178 | 7500 Mpa | |
| Charpy Notched Impact Strength | ISO179 | 8.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179 | 60.0 kJ/m² | |
| elongation at break | ISO527 | 2.0 % |
| other | Test Condition | Test Method | 浙江新力/TS550G6A Nature |
|---|---|---|---|
| Linear forming shrinkage rate | ISO2577 | 0.8 % | |
| Surface Resistivity | IEC60093 | 1.00E+13 Ω | |
| proof tracking index | 3mm | IEC60112 | V |
| Flame retardant performance | Test Condition | Test Method | 浙江新力/TS550G6A Nature |
|---|---|---|---|
| Flame retardant performance | 厚度1.5mm | UL 94 | ℃ |
| 厚度0.8mm | UL 94 | ℃ | |
| 厚度3.0mm | UL 94 | ℃ | |
| 厚度2.0mm | UL 94 | ℃ | |
| GWFI | 厚度1.5mm | IEC60695-2-12 | ℃ |
| 厚度3.0mm | IEC60695-2-11 | ℃ | |
| 厚度0.8mm | IEC60695-2-12 | ℃ | |
| 厚度2.0mm | IEC60695-2-12 | ℃ |
| physical property | Test Condition | Test Method | 浙江新力/TS550G6A Nature |
|---|---|---|---|
| Water absorption rate | ISO62 | 0.1 % | |
| density | ISO1183 | 1.53 g/cm³ |
| Thermal performance | Test Condition | Test Method | 浙江新力/TS550G6A Nature |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa | ISO76 | ℃ |
| 1.8MPa | ISO76 | 195 ℃ |